Unalloyed Carbon Steel, Carbon Steel, Steel manufacturer / supplier in China, offering High Quality AISI 1330 Unalloyed Carbon Steel, En10025-6 S690q 1.8931 Structural Steel Plate, S890ql, 1.8983 High Strength Low Alloy Steel Plate and so on.

Gold Member Since 2016
Audited Supplier

High Quality AISI 1330 Unalloyed Carbon Steel

Get Latest Price
Min. Order / Reference FOB Price
1 Ton US $800/ Ton
Port: Shanghai, China
Production Capacity: 5000 Tons Per Month
Payment Terms: L/C, T/T
Type: Steel Plate
Standard: ASTM, AISI, GB, JIS, DIN, BS
Certification: ISO, RoHS, IBR
Surface Treatment: Coated
Technique: Hot Rolled
Application: Mold & Dies, Ship Plate, Boiler Plate, Container Plate, Flange Plate

You Might Also Like

Loading...

Basic Info

Model NO.: 1.1170
Special Use: Cutting Tools, Measuring Tools, Cutters in Common Steel, High-strength Steel Plate, Wear Resistant Steel, Silicon Steel
Stock: Stock
Trademark: Baosteel
Transport Package: Standard Seaworthy Package or as The Customer′s Re
Specification: carbon steel
Origin: China
HS Code: 7201200000

Product Description


Designation by Standards
Brand NameRavne No.Mat. No.DINENAISI
28MN67781.117028Mn6-1330
Chemical Composition (in weight %)
CSiMnCrMoNiVWOthers
0.28max. 0.401.48max. 0.40max. 0.10max. 0.40--(Cr+Mo+Ni)=max. 0.63
Description
Manganese steel for moderate and lower temperature use in pressure vessels.
Applications
Used for weld fabrication of pressure vessels that require improved notch toughness for lower than ambient temperature service. Low and moderately stressed parts for vehicles, machines and engines. 
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210 
Density [g/cm3]: 7.83
Soft Annealing
This will produce a maximum Brinell hardness of 223.
Normalizing
Normalizing temperature: 850-890oC.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 830-870oC followed by water or oil quenching.
Tempering
Tempering temperature: 540-680oC
Mechanical Properties in Normalized Condition
Diameter
(mm)
0.2 % proof stress
min.(N/mm2)
Tensile strength
min. (N/mm2)
Elongation
min.(%)
up to 1634563017
17-4031068018
41-10029059018
Mechanical Properties in Quenched and Tempered Condition
Diameter
(mm)
0.2 % proof stress
min. (N/mm2)
Tensile strength
min. (N/mm2)
Elongation
min.(%)
Reduction of area
min. (%)
Notch impact energy (ISO-V) min. (J)
up to 16590800-950134035
17-40490700-850154540
41-100440650-800165040
101-160390590-74018--
161-250390590-74018--
251-500340540-69019--
Hardenability Diagram
Hardenability in the end-quench test
Quenching temperature in the end-quench test is 850oC
Hardness1.5357911131520253035404550
H max.545351484441383531292726252524
H min.4542372721----------
HH max.545351484441383531292726252524
HH min.4846423430272421-------
HL max.514946413532292220------
HL min.4542372721----------