Shanghai, China
Business Range:
Construction & Decoration, Manufacturing & Processing Machinery, Metallurgy, Mineral & ...
Registered Capital:
4.58 Million USD
Management System Certification:
ISO9001:2008
Main Markets:
South America, Southeast Asia/ Mideast, Australia, Domestic
OEM/ODM Service
Sample Available
Overseas Agent / Branch
French Speaker

Steel Plate, Plate, Alloy Steel Plate manufacturer / supplier in China, offering 3m, 4m, 6m AISI M35 Steel, En10025-6 S690q 1.8931 Structural Steel Plate, S890ql, 1.8983 High Strength Low Alloy Steel Plate and so on.

Gold Member Since 2016
Audited Supplier

3m, 4m, 6m AISI M35 Steel

Get Latest Price
Min. Order / Reference FOB Price
1 Ton US $1,200/ Ton
Port: Shanghai, China
Production Capacity: 2000tons/Month
Payment Terms: L/C, T/T
Type: Steel Plate
Standard: AISI, ASTM, DIN, JIS, GB, BS
Composition: Stainless Steel Scrap
Technique: Hot Rolled
Shape: Plate
Surface Treatment: Coated

You Might Also Like

Loading...

Basic Info

Model NO.: M35
Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
Application: Ship Plate
Trademark: Baosteel
Transport Package: Standard Seaworthy Package or as The Customer′s Re
Specification: 50kg
Origin: China
HS Code: 7201500010

Product Description


Designation by Standards
Brand NameRavne No.Mat. No.DINENAISI
BRCMO8821.3243S6-5-2-5HS6-5-2-5M35
Chemical Composition (in weight %)
CSiMnCrMoNiVWOthers
0.91max. 0.45max. 0.404.15-1.906.30-Co: 4.75
Description
M35 is molybdenum high speed steel. Very high resistance to wear and to softening at elevated temperatures. High resistance of cutting edge and good toughness. Deep hardening response. High hot hardness. 
Applications
Highly stressed drills, milling cutters, profile cutting tools, thread cutting drills and cold forming tools. 
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 217 
Density [g/cm3]: 8.1
Thermal conductivity [W/m.K]: 19.0 
Electric resistivity [Ohm mm2/m]: 0.60
Specific heat capacity[J/g.K]: 0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC20-200oC20-300oC20-400oC20-500oC20-600oC20-700oC
9.710.511.011.411.512.012.5
Soft Annealing
Heat to 820-880oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230-300.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Heat to 450-600oC, preheat to 850oC and then to 1050oC. Harden from a temperature of 1210-1250oC followed by oil, air quenching or warm bath 550oC. Hardness after quenching is 64-66 HRC.
Transformation temperatures: Ac1=824oC , Ac3=853oC.
Tempering
Tempering temperature: 3 x 1 hour at 540-570oC.
Tempering Temperature (oC) vs. Hardness (HRC)
200oC300oC400oC500oC525oC550oC575oC600oC650oC700oC
6361626464.56564635546

Send your message to this supplier

*From:
*To:
avatar Miss Janet Chang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now