Audited Supplier N06601 High Grade Nickel Based Alloy Pipe is outlined in the following table.
| Element | Content (%) |
|---|---|
| Nickel, Ni | 58-63 |
| Chromium, Cr | 21-25 |
| Aluminum, Al | 1-1.7 |
| Copper, Cu | 1 |
| Manganese, Mn | 1 |
| Silicon, Si | 0.5 |
| Carbon, C | 0.1 |
| Sulfur, S | 0.015 |
| Iron, Fe | Balance |
The following table shows the physical properties of N06601 High Grade Nickel Based Alloy Pipe.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.11 g/cm3 | 0.293 lb/in3 |
| Melting point | 1360-1411°C | 2480-2572°F |
The mechanical properties of N06601 High Grade Nickel Based Alloy Pipe are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (Solution annealed) | 760 MPa | 110000 psi |
| Yield strength (Solution annealed) | 450 MPa | 65300 psi |
| Elongation at break (Solution annealed) | 42% | 42% |
The thermal properties of N06601 High Grade Nickel Based Alloy Pipe are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 13.75 µm/m°C | 7.639 µin/in°F |
| Thermal conductivity | 11.2 W/mK | 77.7 BTU.in/hrft².°F |
Conventional machining techniques that are used for machining iron-based alloys can be used.
N06601 High Grade Nickel Based Alloy Pipe has excellent ductility, and can be readily formed by all conventional techniques.
The alloy can be welded using commonly used welding techniques such as gas-tungsten arc welding, shielded metal-arc welding, gas metal-arc welding and submerged-arc welding.
The alloy can be forged in the temperature range of 1038 to 1232°C (1900 to 2250°F).
Hot working of nicrofer 6023 alloy can be performed in the temperature range of 871 to 1232°C (1600 to 2250°F).
Cold working may be performed using standard tooling.
The alloy can be annealed at 1149°C (2100°F) and then rapidly cooled to avoid thermal cracking.
Other designations that are equivalent to nicrofer 6023 alloy include the following:
The following are the list of applications of nicrofer 6023 alloy:
Stock
|
Form |
Specification |
Supply Form |
Others |
|
Sheet |
Thickness:0.40-4.75mm,General Width:1000,1219,1500mm |
Whole Coil or piece of it |
Cold Annealed,Surface 2B,2E |
|
Plate |
Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,8000,8500mm(Under 10mm plate can be coiled) |
Whole Coil or piece of it |
Single hot rolling,Solid solution annealed state,Surface 1D |
|
Belt |
Thickness:0.10-3.0mm,Width:50-500mm |
Whole Coil or Specified size |
Cold Annealed,Surface 2B,2E |
|
Bar & Rod |
Rolled barΦ5-45mm,Length≤1500mm |
Polished Bar(circle,Square) |
Solution annealing,descaling |
|
Forged barΦ26-245mm,Length≤4000mm |
|||
|
Weld tube |
Outer diameterΦ4.76-135mm,Wall Thickness0.25-4.00mm,Length:≤35000 mm |
Base on your requirement |
Use for PHE |
|
Seamless Tube |
Outer diameterΦ3-114mm,Wall Thickness0.2-4.5mm |
Base on your requirement |
Use for PHE |
|
Wire |
Outer diameterΦ0.1-13mm |
Base on your requirement |
Ni & Ni alloy, Ti & Ti alloy |
|
Forged piece |
roundness and square alloy |
Base on your requirement |
Steel, Alloy |
|
Flangs |
All kinds of Flangs |
Base on your requirement |
Steel, Alloy |
|
Welding Material |
Coil wire Φ0.90mm/1.2mm/1.6mm |
Base on your requirement |
Certificate of Origin:America, Sweden, Britain, Germany, Austria, Italy, France. |
|
Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm |
|||
|
Welding rodΦ2.4mm/3.2mm/4.0mm |
|||
|
Tube |
Elbow, three links, four links, different diameter size |
Base on your requirement |
Ni & Ni alloy, Ti & Ti alloy |
|
Explosive bonded laminate |
Raw Sheet Thickness≥2mm |
Base on your requirement |
Ni & Ni alloy, Ti & Ti alloy |
4. Contact us
Name: Denny Cheng
Direct line: 021-67897611
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}